输送带损伤要注意的修复方式!

来源:http://www.huafengxiangsu.com 时间:2021-11-17 13:46:50 浏览次数:
一、修补条含半硫化层,与皮带超强粘接,抗拉强度高,快速修复,操作简便,节约时间 ,即修即用。适用于传送带长距离划伤、划透及边缘磨损的修复、局部橡胶层损伤修复,皮带冷无缝搭接的封口等方面。它分为加强型与非加强型。
1、 The repair strip contains semi vulcanized layer, which is super bonded with the belt, with high tensile strength, rapid repair, simple operation and time saving. It is applicable to the repair of long-distance scratch, penetration and edge wear of conveyor belt, the repair of local rubber layer damage, the sealing of cold seamless lap of belt, etc. It is divided into reinforced and non reinforced.
二、修补条的用途
2、 Purpose of patch strip
用于修补各类输送带的纵向撕裂、皮带冷硫化接头封口处理。与冷硫化粘接剂配合使用,适用于橡胶传送带纵向划伤、边缘破损及撕裂的修补和橡胶传送带的冷硫化搭接(皮带接头)的封口。
It is used for repairing longitudinal tear of various conveyor belts and sealing of belt cold vulcanization joints. Used together with cold vulcanization adhesive, it is suitable for the repair of longitudinal scratches, edge damage and tears of rubber conveyor belt and the sealing of cold vulcanization lap (belt joint) of rubber conveyor belt.
三、特点
3、 Characteristics
抗拉耐磨,背面预制半硫化层(带CN层或带半硫化层)带织物层的抗拉强度、耐磨、耐热、耐燃、耐辐射好的皮带修补条,粘接面可涂刷冷硫化粘接剂,即修即用。适用于皮带输送带长距离划伤、划透及边缘磨损的修复、局部橡胶层损伤修复,皮带无缝搭接的封口等方面。
Tensile and wear-resistant, prefabricated semi vulcanized layer on the back (with CN layer or semi vulcanized layer) belt repair strip with good tensile strength, wear resistance, heat resistance, flame resistance and radiation resistance of fabric layer, and the bonding surface can be coated with cold vulcanization adhesive for immediate repair and use. It is applicable to the repair of long-distance scratch, penetration and edge wear of belt conveyor belt, the repair of local rubber layer damage, the sealing of seamless lap of belt, etc.
输送带损伤的几种原因分析及修复方法
Several causes analysis and repair methods of conveyor belt damage
众所周知,输送带在长期的使用过程中,难免会遇到输送带纵向撕裂、输送带龟裂、输送带带面的损伤,大家称之为输送带常规损伤,每次看到这种情况都是很头疼的,轻的话做一些冷硫化修补,重的话就要对皮带进行更换、进行热硫化接头了。不但给自己造成麻烦,更重要的是给企业造成了不必要的经济损失。那么如何避免这些情况的发生呢?下面大家就简单地分析一下其中的原因吧。
As we all know, during the long-term use of the conveyor belt, it is inevitable to encounter the longitudinal tear of the conveyor belt, the crack of the conveyor belt and the damage of the conveyor belt surface. We call it the conventional damage of the conveyor belt. It is a headache every time we see this situation. If it is light, do some cold vulcanization repair, and if it is heavy, replace the belt and carry out hot vulcanization joint. It not only caused trouble to itself, but also caused unnecessary economic losses to the enterprise. So how to avoid these situations? Let's simply analyze the reasons.
山东输送带皮带
一、输送带纵向撕裂的原因:
1、 Causes of longitudinal tear of conveyor belt:
一)、振动冲击引起紧固件松动和脱落,造成落煤管衬板、导料板等坠落。
1) . the vibration and impact causes the fasteners to loosen and fall off, resulting in the falling of coal drop pipe lining plate, guide plate, etc.
二)、物料内混入异物,异物坚硬,有棱角,落煤管堵塞挤死。
2) . foreign matters are mixed in the material, which are hard and angular, and the coal chute is blocked and squeezed.
三)、托辊缺损,托辊架造成划伤。
3) . the idler is damaged and the idler frame is scratched.
四)、输送带严重跑偏后被机架挂住。
4) . the conveyor belt is caught by the frame after serious deviation.
五)、清扫器卷入滚筒(回称清扫器),螺栓松动,有弹跳的先兆。
5) The sweeper is drawn into the drum (back to the sweeper), the bolts are loose and there is a sign of bouncing.
二、输送带龟裂的原因:
2、 Causes of belt cracking:
一)、由于受空间尺寸的限制,输送带的弯曲次数多。
1) Due to the limitation of space size, the conveyor belt has many bending times.
二)、接头硫化时由于种种原因进行过两次以上的硫化。
2) The joint has been vulcanized more than twice due to various reasons.
上一篇:耐切割输送带有哪些常识?
下一篇:最后一页

产品中心 PRODUCT CENTER

联系大家CONTACT US

手机:13964193999(孙经理)
座机:0531-83510047
QQ(客服):136559297
地址:山东省济南市章丘区刁镇民营经济开发区

vns85978威尼斯城官网|威尼斯城所有登入网址

XML 地图 | Sitemap 地图